WELDFAST SERIES
STAINLESS STEEL ELECTRODE
 
WELDFAST 308 WELDFAST 317L WELDFAST 310 WELDFAST 410Ni-Mo
WELDFAST 308L WELDFAST 309 WELDFAST 312 WELDFAST 430
WELDFAST 308Mo WELDFAST 309L WELDFAST 318 WELDFAST 630
WELDFAST 347 WELDFAST 309Mo WELDFAST 320 WELDFAST 2209
WELDFAST 316 WELDFAST 309MoL WELDFAST 13 WELDFAST 2594
WELDFAST 316L WELDFAST 309Cb WELDFAST 410 WELDFAST 2553
            WELDFAST 307S
 
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 308
AWS A/SFA - 5.4 E 308-16
IS 5206 / E19.9R26
A rutile basic coated all position electrode. Smooth arc, excellent slag
removal, smooth uniform bead and easy striking are the characteristics of
this electrode.
Re-drying temperature is 300°C for 1 hr.

Approvals : RDSO : CLASS M1
C : 0.08 max
Mn : 0.60-1.20
Si : 1.00 max
Ni : 9.00-11.00
Cr : 18.00-21.00
S : 0.03 max
P : 0.04 max
UTS : 560-630 N/mm2
Elongation : 35-40%
Ferrite (%) : 3-7
Current : AC/DC+
For welding of corrosion resistant Cr-Ni steels of AISI
grades 301, 302, 304, 308 used in dairy, food
processing and chemical industries.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 308L
AWS A/SFA - 5.4 E 308L-16
IS 5206 / E19.9LR26
A rutile basic coated all position electrode. Excellent slag removal, smooth & uniform bead and easy striking are the characteristics. Extra low carbon content gives added resistance to inter granular corrosion.

Re-drying temperature is 300°C for 1 hr.

Approvals : NPCIL
C : 0.04 max
Mn : 0.60-1.20
Si : 1.00 max
Ni : 9.00-11.00
Cr : 18.00-21.00
S : 0.03 max
P : 0.04 max
U T S : 540-580 N/mm2
Elongation : 35-40%
Ferrite (%) : 3-7
Current : AC/DC+
For welding of Cr-Ni steels of AISI grades 301, 302,
304, 308 equipments used in chemical processing,
dairy & food industry.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 308Mo
AWS A/SFA - 5.4 E 308Mo-16
IS 5206 / E19.9.2R26
A rutile basic coated all position electrode. Smooth arc, easy slag removal, uniform bead and easy striking are the characteristics of this electrodes.

Re-drying temperature is 300°C for 1 hr.
C : 0.08 max
Mn : 0.80-1.20
Si : 1.00 max
Ni : 9.00-11.00
Cr : 18.00-21.00
Mo : 2.00-3.00
S : 0.03 max
P : 0.04 max
UTS : 630-730 N/mm2
Elongation : 35-40%
Current : AC/DC+
For welding of steels where severe stresses or risk of cracking are involved.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 347
AWS A/SFA - 5.4 E 347-16
IS 5206 / E19.9NbR26
A rutile basic coated all position electrode for welding stabilized version of corrosion resistant Cr-Ni Steels. Weld beads are smooth, uniform and excellent in appearance.

Re-drying temperature is 300°C for 1 hr.
C : 0.08 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 9.00-11.00
Cr : 18.00-21.00
Cb : 1.00 max
S : 0.03 max
P : 0.03 max
UTS : 560-620 N/mm2
Elongation : 30-35%
Ferrite (%) : 6-9
Current : AC/DC+
For welding of AISI grades 301, 302, 304, 308, 321 and 347. A wide range of application in the manufacture
of equipments for chemical, food, aircraft industries,
gas turbines and soap industries.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 316
AWS A/SFA - 5.4 E 316-16
IS 5206 / E19.12.2R26
A rutile basic coated all position electrode, 18/12 Mo Stainless Steel weld
deposit. The weld metal has excellent creep strength and resistance to cracking, corrosion at high temperature up to 850°C. The electrode has smooth arc & excellent arc stability, low spatter loss, easy removal of slag and smooth, uniform weld deposit.

Re-drying temperature is 300°C for 1 hr.
C : 0.08 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 11.00-14.00
Cr : 17.00-20.00
Mo : 2.00-3.00
S : 0.03 max
P : 0.03 max
UTS : 580-630 N/mm2
Elongation : 30-35%
Ferrite (%) : 3-8
Current : AC/DC+
For welding of corrosion resistant Cr-Ni-Mo Steels of
AISI grades 316, 316H, 317 used in chemical industries, handling organic assets and other
corrosion chemicals etc.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 316L
AWS A/SFA - 5.4 E 316L-16
IS 5206 / E19.12.2LR26

A rutile basic coated all position electrode having extra low carbon
with weld deposit of 18Cr/13Ni/2.5Mo stainless steel. Resistant to stress corrosion cracking, chemical corrosion cracking at temperature up to
850°C. The weld metal deposit has excellent creep strength and is of
radiographic quality.
Re-drying temperature is 300°C for 1 hr.

Approvals : NPCIL

C : 0.04 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 11.00-14.00
Cr : 17.00-20.00
Mo : 2.00-3.00
S : 0.03 max
P : 0.03 max
U T S : 560-600 N/mm2
Elongation : 30-40%
Ferrite (%) : 3-8
Current : AC/DC+
For welding of stainless steels such as AISI 316, 316L, 316H, 317 and 317L, in chemical plants, paint industries and dye industries.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 317L
AWS A/SFA - 5.4 E317L-16

A rutile basic coated all position electrode having extra low carbon with
weld deposit of 19Cr/12Ni/3.5 Mo and controlled Ferrite content of 3-8 for
maximum resistance to cracking. Weld Metal is resistant to stress corrosion cracking, hot cracking, chemical corrosion at high temp. Higher moly reduces susceptibility to pitting. Excellent arc stability and low spatter loss. The weld metal is of radiographic quality.

Re-drying temperature is 300°C for 1 hr.

C : 0.04 max
Mn : 0.50-2.50
Si : 1.00 max
Ni : 12.00-14.00
Cr : 18.00-21.00
Mo : 3.00-4.00
S : 0.03 max
P : 0.03 max
UTS : 560-600 N/mm2
Elongation : 30-40 %
Ferrite (%) : 3-8
Current : AC/DC+
For welding of stainless steels such as AISI
316L/317and for welding of equipments in chemical industries especially for sulphuric and sulfurous acids and their salts, paper and pulp industry, paint and dye industries.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 309
AWS A/SFA - 5.4 E 309-16
IS 5206 / E23.12R26

A rutile basic coated all position electrode giving 25/12, Cr-Ni deposit
which has excellent corrosion and oxidation resistance in continuous
service up to 1100°C. It gives smooth arc and has self - removing slag, least spatter and uniform weld bead.

Re-drying temperature is 300°C for 1 hr
.
Approvals : RDSO : CLASS M4

C : 0.10 max
Mn : 0.60-1.20
Si : 1.00 max
Ni : 12.00-14.00
Cr : 22.00-25.00
S : 0.03 max
P : 0.03 max
UTS : 550-650 N/mm2
Elongation : 30-35%
Current : AC/DC+
For welding of corrosion and heat resistant Cr-Ni
steels to themselves or to mild steel. The weld
deposit offers higher temperature oxidation
resistance than 18/8 Cr-Ni grade stainless steel. It is
used for overlays of ferritic steel, dissimilar steels and difficult to weld steels.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 309L
AWS A/SFA - 5.4 E 309L-16
IS 5206 / E23.12LR26

A rutile basic coated all position electrode giving 25/12, Cr-Ni deposit
which has excellent corrosion and oxidation resistance in continuous
service up to 1100°C. It gives smooth arc, self removal of slag, least spatter and uniform weld bead. The extra low carbon gives added resistance to
inter-granular corrosion.

Re-drying temperature is 300°C for 1 hr.

Approvals : NPCIL

C : 0.04 max
Mn : 0.60-1.20
Si : 1.00 max
Ni : 12.00-14.00
Cr : 22.00-25.00
S : 0.03 max
P : 0.03 max
UTS : 520-650 N/mm2
Elongation : 30-35%
Current : AC/DC+
For welding of corrosion and heat resistant Cr-Ni
steels to themselves or to mild steel. The weld
deposit offers higher temperature oxidation
resistance than 18/8 Cr-Ni grade stainless steel.
Useful in welding of clad steel.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 309Mo
AWS A/SFA - 5.4 E 309Mo-16
IS 5206 / E23.12.2R26

A rutile basic coated all position electrodes giving 25/12/2.5 Mo weld
deposit. It gives a smooth arc, low spatter, easy removal of slag and uniform
bead.

Re-drying temperature is 300°C for 1 hr.

Approvals : NPCIL

C : 0.10 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 12.00-14.00
Cr : 22.00-25.00
Mo : 2.00-3.00
S : 0.03 max
P : 0.03 max
UTS : 550-650 N/mm2
Elongation : 30-35%
Current : AC/DC+
For welding of corrosion and heat resistant Cr-Ni
steels to themselves or to mild steel. The electrode
is useful in welding clad steel and for building
corrosion and heat resistant layer on mild or low alloy steels. Also suitable for dissimilar joints of
carbon steels with 316 type of stainless steel.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 309MoL
AWS A/SFA - 5.4 E 309L-Mo-16
IS 5206 / E23.12.2LR26

A rutile basic coated all position electrode giving 25/12/2.5 Mo weld
deposit. It gives a smooth arc, low spatter, easy removal of slag and uniform bead. Excellent resistance to chemical corrosion and heat.

Re-drying temperature is 300°C for 1 hr.

C : 0.04 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 12.00-14.00
Cr : 22.00-25.00
Mo : 2.00-3.00
S : 0.03 max
P : 0.03 max
UTS : 520-650 N/mm2
Elongation : 30-35%
Current : AC/DC+
For welding of corrosion and heat resistant Cr-Ni
steels to themselves or to mild steel. The electrode is
useful in welding clad steel and for building
corrosion heat resistant layer on mild or low alloy
steels.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 309Cb
AWS A/SFA - 5.4 E 309Cb-16
IS 5206 / E23.12CbR26

It is rutile basic coated all position electrode gives smooth arc, easy slag
removal and uniform weld bead. It gives weld deposit of 25/12Cb stabilised SS which has excellent resistant to inter-granular corrosion and higher strength upto 1100°C.

Re-drying temperature is 300°C for 1 hr.

C : 0.10 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 12.00-14.00
Cr : 22.00-25.00
Cb : 0.70-1.00
S : 0.03 max
P : 0.03 max
UTS : 580-650 N/mm2
Elongation : 30-35%
Current : AC/DC+
For welding of corrosion and heat resistant Cr and
Cr-Ni stabilized steel to themselves or to mild steel.
Welding of AISI 309-Cb, SS 347 to low alloy or carbon
steels. The electrode is useful in welding clad steels.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 310
AWS A/SFA - 5.4 E 310-16
IS 5206 / E25.20R26X

A basic coated austenitic all position electrode and deposit 25/20 SS which
has excellent stability and oxidation resistance in continuous service upto 1100°C. Smooth arc, easy slag removal, low spatter and uniform bead are characteristics of this electrode.

Re-drying temperature is 300°C for 1 hr.

C : 0.10-0.15
Mn : 1.00-2.50
Si : 0.75 max
Ni : 20.00-22.50
Cr : 25.00-28.00
S : 0.03 max
P : 0.03 max
UTS : 550-580 N/mm2
Elongation : 30-35%
Current : AC/DC+
Welding of AISI 310 type, German steels 4762,
4828, 4841, 4846 and 4848 welding of stainless clad
steels, straight chrome steels, dissimilar steels,
hydrogenation and polymerisation plant, gas turbine combustion chamber parts, high temp.
furnace parts etc.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 312
AWS A/SFA - 5.4 E 312-16
IS 5206 / E28.8R26

A rutile basic coated all position electrode giving 30/10 Cr-Ni deposit which has excellent oxidation resistance. The weld deposit gives duplex structure with substantial amount of Ferrite in austenitic matrix. The deposited weld metal is highly resistant to cracks and fissures. It gives smooth and stable arc, low spatter, easy removal of slag & uniform weld bead.

Re-drying temperature is 300°C for 1 hr.

C : 0.08-0.15
Mn : 0.90-1.30
Si : 0.90 max
Ni : 8.00-10.50
Cr : 28.00-32.00
S : 0.03 max
P : 0.04 max
UTS : 750-800 N/mm2
Elongation : 22 % (min)
Current : AC/DC+
For welding of all unknown composition and dissimilar joints. Extensive application in heavy mining and earth moving equipments. The weld deposit has very high strength in addition to moderate corrosion resistance.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 318
AWS A/SFA - 5.4 E318-16
IS 5206 / E19.12.2NbR26

A rutile basic coated all position electrode for welding stabilized version of corrosion resistant Cr-Ni-Mo Steels. The electrode is resistant to stress
corrosion cracking, chemical corrosion and inter-granular corrosion. The weld metal has excellent creep strength up to 850°C and is of radiographic quality. Weld beads are smooth uniform and excellent in appearance.

Re-drying temperature is 300°C for 1 hr.

C : 0.08 max
Mn : 0.60-1.20
Si : 0.90 max
Ni : 11.00-14.00
Cr : 17.00-20.00
Mo : 2.00-3.00
Cb : 1.00 max
S : 0.03 max
P : 0.04 max
UTS : 600-650 N/mm2
Elongation : 25-30%
Ferrite (%) : 4-8
Current : AC/DC+
For welding of stainless steels such as AISI 316, 317, 318 and CPF 8M, CPF 10MC, CPF 8C and CPF 8M, paper industries, bleaching equipments, chemical plants handling sulphuric, hydrochloric, acetic, formic, citric, tartaric acid etc., dyeing equipments,
pickling plant, heat resistant casting.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 320
AWS A/SFA - 5.4 E 320-15

A medium heavy coated basic type all position electrode giving a smooth arc, medium penetration and least spatter. The slag is easily removable and
has a smooth and uniform bead. The weld metal can withstand
temperature up to 1200°C in continuous service. Excellent resistance to chemical corrosion and heat.

Re-drying temperature is 300°C for 1 hr.

C : 0.07 max
Mn : 1.20-1.80
Si : 0.60 max
Ni : 32.0-36.0
Cr : 19.0-21.0
Mo : 2.00-3.00
Cu : 3.00-4.00
Cb : 1.00% max
S : 0.03 max
P : 0.03 max
UTS : 550-600 N/mm2
Elongation : 30 % min
Current : DC+
For welding cast or wrought heat resistant alloys like
HV9, carpenter 20. Application for a wide range of chemical plants handling sulphuric and sulphurous acids and their salts.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 13
AWS A/SFA - 5.4 E 410-15

A heavy basic coated electrode, specially designed for welding of ferritic martensitic chrome steels. The weld metal contains 13% Cr and air
hardenable. Hardening can be avoided through preheating and stress
relieving.

Re-drying temperature is 300°C for 1 hr.

C : 0.06-0.09
Mn : 0.50-0.90
Si : 0.40-0.60
Cr : 11.0-13.0
S : 0.03 max
P : 0.04 max
UTS : 530-580 N/mm2
Elongation : 23-27%
Current : DC+
For joining of heavy section of steel armatures, welding of similar corrosion resistant Cr Steels and steels casting. It is also used in pump parts, oil refinery equipments, coal washers and general
corrosion & heat resisting applications.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 410
AWS A/SFA - 5.4 E 410-15

A basic coated electrode with ER410 core wire for welding of 13% Cr Steels
for producing straight chrome stainless steel deposit on austenitic
stainless steels and carbon steels. The weld deposit is of air hardening type
and requires preheat and post heat treatment to achieve optimum
ductility and toughness to resist cavitation-erosion, abrasion and
moderate corrosion.

Re-drying temperature is 300°C for 1 hr.

C : 0.10 max
Mn : 1.00 max
Si : 0.90 max
Cr : 11.00-13.50
S : 0.03 max
P : 0.04 max
UTS : 520-570 N/mm2
Elongation : 24-28%
Current : DC+
Very much suitable for refiner plug and socket, sleeves, turbine runners, valve seats etc.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 410Ni-Mo
AWS A/SFA - 5.4
E 410Ni Mo -15 (Nearest)

A basic coated all position electrode. It gives smooth arc, easy removal of slag and uniform weld bead. The weld deposit is of radiographic quality.

Re-drying temperature is 300°C for 1 hr.

C : 0.05 max
Mn : 0.60-0.90
Si : 0.30-0.60
Cr : 11.5-14.0
Mo : 0.40-0.60
Ni : 3.80-5.50
S : 0.03 max
P : 0.03 max
UTS : 790 N/mm2 min
YS : 590 N/mm2 min
Elongation : 14% min
CVN Impact at 23±5°C : 50 J min
CVN Impact at 0°C : 45 J min
Current : DC+
Hardness : 260 BHN

PWHT @ 600°C for 8 hrs is necessary to
achieve desired properties
For welding ASTM CA6NM (CA-6NM) castings or similar materials as well as type 410, 410S and 405 base metals.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 430
AWS A/SFA - 5.4 E 430-15

A basic coated electrode for welding of AISI 430 stainless steel and steels of slightly lower or higher Cr content. Welding with Weldfast 430 electrodes
usually require suitable preheat and post heat treatment to obtain
optimum physical properties of the weldment. The weld deposits are of
radiographic quality.
Re-drying temperature is 300°C for 1 hr.

C : 0.10 max
Mn : 1.00 max
Si : 0.90 max
Cr : 15.0-18.0
Ni : 0.60 max
Mo : 0.75 max
S : 0.03 max
P : 0.03 max.
UTS : 580 min N/mm2
Elongation : 20% min
Current : DC+
For welding of AISI 430 stainless steels, automobile body moulding, oil burner parts, equipments in
chemical & food industries.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 630
AWS A/SFA- 5.4 E 630-16

It offers the combined characteristics of a strong, corrosion resistant, easily
machinable weld metal. This electrode is primarily designed for welding ASTM A-564, type 630 (17Cr, 4 Ni ) and precipitation hardenable steel. The
composition of the weld deposit is modified to eliminate ferrite stringers in the martensitic microstructure that would improve the mechanical
properties. Depending on the weld dimensions and applications, it may
be used in the as welded, welded plus precipitation hardened, or welded plus solution treated plus precipitation hardened condition.

Re-drying temperature is 300ºC for 1 hr.

C : 0.05 max
Mn : 0.25-0.75
Si : 0.75 max
Ni : 4.50-5.00
Cr : 16.0-16.75
Mo : 0.75 max
Nb : 0.15-0.30
Cu : 3.25-4.0
S : 0.03 max
P : 0.04 max
U T S : 1030 N/mm2 min
Elongation : 10% min
Current : DC+
Electrodes of this composition are used in a wide variety of applications including oil field valve
equipment chemical process equipment, fittings, pumpshafts, gears, paper mill equipment, and
aircraft parts.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 2209
AWS A/SFA- 5.4 E 2209-16

It is a rutile basic coated electrodes giving 22.5Cr, 3.00 Mo, 0.12 N which
has excellent corrosion resistant. It gives smooth arc, self removal of slag,
least spatter and uniform weld bead. These electrodes give increased tensile strength with improved resistance to pitting corrosive attack
and to stress corrosion cracking. This electrode is specially designed
for ferritic-austenitic stainless steels or the so called "Duplex stainless
steels".

C : 0.04max
Mn : 0.50-2.00
Si : 1.00 max
Ni : 8.50-10.50
Cr : 21.50-23.50
Mo : 2.50 - 3.50
N : 0.08-0.20
Cu : 0.75 max
S : 0.03 max
P : 0.04 max
U T S : 690 N/mm2 min
Elongation : 20% min
Electrodes of this composition are used primarily to weld duplex stainless steel which contains approximately 22 percent of chromium. It finds extensive use in welding duplex steels which needs
high resistance to stress corrosion cracking and high yield strength e.g. In ship building industry,
chemical industries etc.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 2594
AWS A/SFA-5.4 E 2594-16

Duplex stainless steel all position electrodes giving 25.5 Cr,10.0 Ni, 4.0 Mo,
0.25N deposit gives smooth arc, self removal of slag, least spatter and
uniform weld bead.
Re-drying temperature is 300°C for 1 hr

C : 0.04 max
Mn : 0.50-2.00
Si : 1.00 max
Ni : 8.00-10.50
Cr : 24.0-27.0
Mo : 3.50 - 4.50
N : 0.20 - 0.30
Cu : 0.75 max
S : 0.03 max
P : 0.04 max
U T S : 760 N/mm2 min
Elongation : 15% min
It is designed for welding of type 2507 super duplex
stainless steels and similar composition. It can also be used for the welding of carbon and low alloy steels to duplex stainless steels as well as to weld
standard duplex stainless steels such as type 2205.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 2553
AWS A/SFA- 5.4 E 2553-16

Rutile coated electrode for welding super duplex austenitic ferritic steels.
Weldmetal deposited by these electrode combine increased tensile
strength with improve resistance to pitting corrosive attack and stress corrosion. The electrode deposits weld metal having uniform and fine
ripples. Slag removal is very easy and spatter loss is extremely low.
Electrode works in all positions.

Re-drying temperature is 300 C for 1 hr.

C : 0.06 max
Mn : 0.50-1.50
Si : 1.00 max
Ni : 6.50-8.50
Cr : 24.00-27.00
Mo : 2.90-3.90
N : 0.10-0.25
Cu : 1.50-2.50
S : 0.03 max
P : 0.04 max
U T S : 760 N/mm2min
Elongation : 15% min
It is designed for welding of type 2553 super duplex
stainless steels and similar composition. Welding of super duplex austenitic ferritic stainless steels. Used for piping in gas or oil, offshore platforms.
Product Name / Specification
Characteristics
All Weld Analysis (%) Mechanical Properties Application
WELDFAST 307S
AWS A/SFA 5.4 E307-16
IS 5206 / E18.8MnR26

A high deposition efficiency electrode for depositing extremely tough buffer layer prior to hardfacing or joining of dissimilar sections of almost any composition of steel.

Re-drying temperature is 300 C for 1 hr.

Approvals : RDSO : CLASS M5

C : 0.06-0.10
Mn : 3.30-4.75
Si : 0.50-0.80
Cr : 18.0-21.0
Ni : 9.00-10.70
S : 0.03 max
P : 0.03 max
U T S : 580-620 N/mm2
Elongation : 30 - 35%
Hardness : 180-220 BHN
(As welded)
Hardness : 500 - 550 BHN
(Work hardened)
Current : AC/DC+
Rebuilding of austenitic manganese parts, over laying on cast steels, carbon & alloy steels, diamond
crossings, forging hammer and anvil repair. The deposit can stand heavy impact loading work
hardens in service.
 
www.weldwell.co.in