SOLID STAINLESS STEEL WIRES FOR MIG / TIG WELDING
Brand Name
AWS
Classification
(AWS/SFA-5.9)
WIRE CHEMISTRY (%)
Mechanical Properties of
All W- eld Metal in
As- welded condition
Sizes
(Dia. mm)
C
Cr
Ni
Mn
Si
Mo
Nb
MIGFAST 308/
TIGFAST 308
ER 308
0.08
19.50-22.00
9.00-11.00
1.00-2.50
0.30-0.65
-
-
UTS Mpa
Elongation
550 Min
35% Min
MIGFAST 308L/
TIGFAST 308L
ER 308L
0.03
19.50-22.00
9.00-11.00
1.00-2.50
0.30-0.65
-
-
520 Min
35% Min
MIGFAST 347/
TIGFAST 347
ER 347
0.08
19.00-21.50
9.00-11.00
1.00-2.50
0.30-0.65
-
1Max
520 Min
30% Min
MIGFAST 316/
TIGFAST 316
ER 316
0.08
18.00-20.00
11.00-14.00
1.00-2.50
0.30-0.65
2.00-3.00
-
520 Min
30% Min
MIGFAST 316/
TIGFAST 316 L
ER 316L
0.03
18.00-20.00
11.00-14.00
1.00-2.50
0.30-0.65
2.00-3.00
-
490 Min
30% Min
MIGFAST 309/
TIGFAST 309
ER 309
0.12
23.00-25.00
12.00-14.00
1.00-2.50
0.30-0.65
-
-
550 Min
30% Min
MIGFAST 309L/
TIGFAST 309L
ER 309L
0.03
23.00-25.00
12.00-14.00
1.00-2.50
0.30-0.65
-
-
520 Min
30% Min
MIGFAST 309 Mo/
TIGFAST 309 Mo
ER 309Mo
0.12
23.00-25.00
12.00-14.00
1.00-2.50
0.30-0.65
2.00-3.00
-
550 Min
30% Min
MIGFAST 310/
TIGFAST 310
ER 310
0.08-0.15
25.00-28.00
20.00-22.50
1.00-2.50
0.30-0.65
-
-
550 Min
30% Min
MIGFAST 312/
TIGFAST 312
ER 312
0.15
28.00-32.00
8.00-10.50
1.00-2.50
0.30-0.65
-
-
660 Min
22% Min
MIGFAST 410/
TIGFAST 410
ER 410
0.12
28.00-32.00
-
0.60
00.50
-
-
520 Min *
20% Min *
MIGFAST 430/
TIGFAST 430
ER 430
0.10
15.50-17.00
-
0.60
00.50
-
-
450 Min**
20% Min**
 
Note : Weld metal properties with 100 % Ar gas shielding.
* After PWHT at 75 C for 1 Hr, furnace cooled to 315 C and then air cooled to ambient.
** After PWHT at 77 C for 2 Hr, furnace cooled to 595 C and then air cooled to ambient.
 
 
www.weldwell.co.in